(Bundle Sale)PLA Silk Triple-Color Filament ，1kg (MOQ:10 Rolls,Mixable )

ERYONE Matte PLA Filament, 1.75mm Filament for 3D Printer, 1KG(2.2LBS)/ Spool,

Matte PLA review by  Parliamo di MakerMatte PLA review by INOV3DFeature：The surface of the print has a matte (matte) effect, which is suitable for printing artwork.Specifications：Filament Diameter: 1.75mmTolerance: ±0.03mmPrinting Temperature: 190°C-220°CHeated Bed Temperature: 55-70°CPrinting Speed: 30-100mm/sShowcase: FAQ 1.Q: Why my filament tangles? How can I solve it?A: The tangle of filament isn’t caused by the disordered or the imperfect winding. According to the production technology of filament, the filament winds back and forth (from left to right and then from right to left). Normally, there is no overline tangle. A common cause of tangle is that the filament end is not fixed to the holes of spool. Overline tangle or the changed winding direction make filament tangle. So customers need to fix the filament end to the proper holes of the spool.2.Q: Can PLA be used to print tableware?A: Not recommended. Although PLA is degradable, food-grade raw material, the PLA with toner is non-food grade.3.Q: The nozzle is clogged by PLA, and how can I solve it?  A: Inconstant filament diameter, the lower nozzle temperature and frequent replacement with different kinds of filaments will lead to this problem. So, before you get started, clean the nozzle and turn up the temperature to a proper value.4.Q: My prints have web-like strings (stringing) issues. How can I troubleshoot it?  A: Too high temperature makes the PLA filament melt and flow so fast. Please turn the temperature down to a proper value.  The retracting parameters are improper, so adjust the retracting length and speed.  5.Q: There are too much melted filament around the nozzle. What should I do?  A: This problem can be attributed to over-high temperature, low printing speed, and in the slice software, the nozzle diameter doesn’t match with the extrusion output.6.Q: The PLA filament was perfect when I opened the package. After several times of intermittent printing, my PLA filament snaps by accident during printing. Why?A: Normally, the PLA filament in the printing process will not snap by themselves. However, after being affected by moisture, the degradable material PLA will be more brittle and easier to break, so you should pay attention to dampproof.7.Q: The surface of my print isn’t very smooth, and the extruded filament has inconstant diameters. Why?  A: The printing temperature is too high or too low. The temperature doesn’t match well with the printing speed. You need to adjust the printing speed or temperature.8.Q: Why my PLA-printed objects don't stick to the heated bed? How do I solve?A: The distance between the nozzle and the bed is too far. Make sure your heated bed is leveled and it’s clean. Then judge if the printing temperature and heated bed temperature are too low, and our customers should adjust them to correct ranges.

ERYONE Triple-Color Silk PLA Filament for 3D Printers,1kg (2.2LBS)/Spool 1.75mm,Accuracy +/- 0.03 mm

PLA Filament - 1.75mm±0.03mm (1kg)

ERYONE PLA Filament has the advantages of easy printing, low shrinkage, and excellent layer bonding.Applicable to 99% of 3D FDM printers on the market, friendly to beginners.High purity raw materials, corn. Technical SpecificationPrint Any Model You Want with ERYONE PLA Filament.Material: PLALength:340mDiameter: 1.75mm±0.03mmPrint Temperature: 190-220℃Heated Bed Temperature: 55-70°CRecommended Printing Temperature: 210-220℃Recommended Print Speed: 30-100mNeat WindingThe PLA threads are arranged neatly, without the risk of knotting that making printing more comfortable.Premium QualityMaterial wire diameter 1.75mm±0.03mm, ensure smooth output line, vacuum packaging without bubbles, does not block nozzle, make the printing more smooth.Good AdhesionExcellent first layer adhesion to reduce warpage, shrinkage, curl and print failure.Good Layer BondingGood layer bonding strength makes the printing parts stronger. The printed model has a smooth surface. The Difference between White&Gray&BlackShowcase:FAQ     1.Q: Can PLA be used to print tableware?A: Not recommended. Although PLA is degradable, food-grade raw material, the PLA with toner is non-food grade. If you really want to print a set of tableware, transparent PLA is suggested.2.Q: The nozzle is clogged by PLA, and how can I solve it?  A:  Inconstant filament diameter, the lower nozzle temperature and frequent replacement with different kinds of filaments will lead to this problem. So, before you get started, clean the nozzle and turn up the temperature to a proper value.3.Q: My prints have web-like strings (stringing) issues. How can I troubleshoot it?  A: Too high temperature makes the PLA filament melt and flow so fast. Please turn the temperature down to a proper value.        The retracting parameters are improper, so adjust the retracting length and speed.  4.Q: There are too much melted filament around the nozzle. What should I do?  A: This problem can be attributed to over-high temperature, low printing speed, and in the slice software, the nozzle diameter doesn’t match with the extrusion output.5.Q: The PLA filament was perfect when I opened the package. After several times of intermittent printing, my PLA filament snaps by accident during printing. Why?A: Normally, the PLA filament in the printing process will not snap by themselves. However, after being affected by moisture, the degradable material PLA will be more brittle and easier to break, so you should pay attention to dampproof.6.Q: The surface of my print isn’t very smooth, and the extruded filament has inconstant diameters. Why?  A: The printing temperature is too high or too low. The temperature doesn’t match well with the printing speed. You need to adjust the printing speed or temperature.7.Q: Why my PLA-printed objects don't stick to the heated bed? How do I solve?A: The distance between the nozzle and the bed is too far. Make sure your heated bed is leveled and it’s clean. Then judge if the printing temperature and heated bed temperature are too low, and our customers should adjust them to correct ranges.

(Bundle Sale) PLA Burnt Titanium Triple Color Filament，1kg (MOQ:10 Rolls,Mixable )

Burnt Titanium Triple PLA The Eryone Burnt Titanium Triple PLA filament is a material that exhibits captivating colorchanges under different lighting and angles, creating a unique technological atmosphere andproviding an exceptional visual and tactile experience. This material has excellent toughness, producing no bubbles or odors during the printing process, and is resistant to clogging orwarping, ensuring outstanding shaping results and a smoother printing experience. Additionally, its Z-axis tensile strength reaches 34 MPa, with excellent interlayer adhesion. Part I:Suggests Printing Parameters Parameter Set up Nozzle temperature 190-220 ℃ Bed temperature 55-70℃ Bed materia glass, PEI, spring steel plate Bottom printing temperature 190-220 ℃ Sealed printing Supports open printing; better results with enclosure. Printing speed 30-100mm/s Drying conditions 65-75℃, 12h   Part II: Physical Properties of Materials Property Testing Method Unit Typical Value Density(g/cm³ at 21.5 ° C） ASTM D792 (ISO 1183, GB/T 1033) g/cm³ 1.23 Vicat Softening Temperature(° C) ASTM D1525 (ISO 306 GB/T 1633) ℃ 54 Heat distortion temperature(° C) ASTM D648 1.8MPa 0.45MPa ℃ 53 Glass transition temperature (° C) DSC, 10 ° C/min ℃ 62 Melt Index(g/10 min) 220 ° C, 10kg 240 ° C, 2.16 kg g/10min 6   Part III: Mechanical Properties of Printed Samples Property Test conditions Test standards unit Typical Value Tensile strength X-Y 50mm/min GB/T 1040.4 MPa 52.2 Elastic modulus X-Y 50mm/min GB/T 1040.1-2006 MPa 1737.5 Elongation at break X-Y 50mm/min GB/T 1040.4 % 2.1 Tensile strength X-Z 50mm/min GB/T 1843 MPa 34.2 Elastic modulus X-Z 50mm/min GB/T 1040.1-2006 MPa 1623.7 Elongation at break X-Z 50mm/min GB/T 1040.4 % 1.9 Bending strength 2mm/min GB/T 9341 MPa 82.4 Bending modulus 2mm/min GB/T 9341 MPa 2861.7 Charpy Impact strenght 2.75J GB/T 1843 kJ/m2 3.7   Note: All splines are printed under the following conditions: printing temperature=210 ° C, printing speed=80mm/s, base plate 60° C, filling=100%, nozzle diameter=0.4mm